American-Standard	Chinese-Standard			chemical component（mass fraction，%）										liquefaction temperature,℃		brazing temperature range /℃
AWS	GB	HL	Cu	Ag	Zn	Sn	Fe	Mn	Ni	P	Pb	Al	Si	solidus	liquidus
AWS	GB	HL	Cu	Ag	Zn	Sn	Fe	Mn	Ni	P	Pb	Al	Si	solidus	liquidus
BCuP-1	——	——	margin	——	——	——	——	——	——	4.8-5.2	——	——	——	710	924	788～927
BCuP-2	BCu93P	HL201	margin	——	——	——	——	——	——	7.0-7.5	——	——	——	710	793	732～843
BCuP-3	BCu89PAg	HL205	margin	4.8-5.2	——	——	——	——	——	5.8-6.2	——	——	——	643	813	718～816
BCuP-4	——		margin	5.8-6.2	——	——	——	——	——	7.0-7.5	——	——	——	643	718	691～788
BCuP-5	BCu80PAg	HL204	margin	14.5-15.5	——	——	——	——	——	4.8-5.2	——	——	——	643	802	704～816
BCuP-6	BCu91PAg	HL209	margin	1.8-2.2	——	——	——	——	——	6.8-7.2	——	——	——	643	788	732～816
BCuP-7	——	——	margin	4.8-5.2	——	——	——	——	——	6.5-7.0	——	——	——	643	771	704～816
BCuP-8			margin	17.8-18.0	——	——	——	——	——	6.0-6.7	——	——	——	664	686	714～730
BCuP-9			——	——	——	6.0-7.0	——	——	——	6.0-7.0	——	——	——	643	693	693～740

The melting temperature of Cu-based non-phosphorus filler metal is higher. Commonly used for brazing carbide, stainless steel and alloy copper base brazing filler metal, mostly based on copper zinc alloy, adding manganese, nickel and other elements to improve its brazing strength, is a brazing carbide performance of better brazing filler metal. Copper base phosphorus containing filler metal, phosphorus content is the key to determine the melting range and performance, can be used as a self-soldering agent in the welding of copper and copper, without adding flux, with good fluidity. However, when brazing brass and bronze, it is necessary to cooperate with the flux. According to the market demand, phosphorus copper filler metal with various composition ratio can be provided.

Specification

Ring: the filament is 0.5mm thin
Ring inner diameter 1.0mm-60mm

All kinds of brazing metal have straight wire, coil wire, sheet, pellet, block, ring and other supply states, All can be customized according to actual needs.